The improvement of the slow kinetics of the oxygen evolution reaction (OER) is extremely important for promoting the efficiency of various energy storage technologies, such as photo/electricity-driven water splitting and rechargeable metal-air batteries. Although marked advances in the development of heterogeneous catalysts to accelerate the OER, progress in real device applications still requires innovations in catalyst design for better-performing properties. Manipulating defect chemistry has been widely seen to tune the properties and functionalities of materials. In particular, vacancy defect engineering can lead to substantial structural perturbations in catalysts, with the capability to tailor surface electronegativity, charge concentration and redistribution, enabling enhanced reactivity. Creating new kind of vacancies in existing catalysts could produce catalytically active sites and provide opportunities for designing better OER catalysts, but it is still a big challenge.
A research team led by Prof. YU Shuhong and Prof. GAO Minrui from the University of Science and Technology of China (USTC) proposes a simple and effective method to create unconventional CN vacancies (VCN) in Ni-Fe Prussian blue analogue (PBA) by a nitrogen plasma bombardment process.Such VCN is largely distinct from the well-studied vacancies previously documented, which not only tunes the local electronic structure and coordination environment of the Ni-Fe sites, but also limits the loss of Fe element during OER process; these together enable a new, robust and high-performance Ni-Fe oxyhydroxide from PBA pre-catalyst during OER. This work was published on Nature Communications entitled as Unconventional CN vacancies suppress iron-leaching in Prussian blue analogue pre-catalyst for boosted oxygen evolution catalysis on June 26th (Nature Communications 2019, 10,2799).
Fig. 1.Schematic illustration of the preparation and structure of VCN-mediated Ni-Fe PBA.
Researchers started with the NiMoO4 nanorods as precursors to prepare Ni-Fe PBA porous nanorods by an ion exchange process. Afterwards, VCN was formed by the direct N2 plasma bombardment. Various characterization techniques, including high-resolution transmission electron microscopy, positron annihilation spectroscopy, elemental content analysis, and the tail gas detection, have confirmed the formation of VCN(Fig. 1).
Electrochemical tests revealed that PBA bombarded by N2 plasma for 60 minutes (PBA-60) had the best OER activity with an onset overpotential of 225 mV and an overpotential of 283 mV at 10 mA cm-2, much better than other studied catalysts. The high OER catalytic activity can be attributed to the coordinatively unsaturated Ni and Fe sites induced by VCN. Meanwhile, OER stability tests revealed that [Fe(CN)6]4-groups in VCN-free PBA (PBA-0) readily diffuse outward to the electrolytes during OER via anion exchange with OH-ions, causing Fe loss in the structure, whereas the unsaturated Fe site in PBA-60 can bond with oxygen to yield Fe-O bonds, preventing the Fe loss during OER, which enables the catalyst to perform very robustly for a long-term stability tests.
Researchers anticipate that the CN vacancies described here not unique to Ni-Fe PBAs, but bears general implications for other catalyst systems with CN groups. This will aid the development of newly advanced catalysts for modern energy devices, which will inspire other researchers to develop a new path for the design of better-performing OER catalysts that are low-cost and readily synthesized.
This work was supported by the funding support from the National Natural Science Foundation of China, the Users with Excellence and Scientific Research Grant of Hefei Science Center of CAS, the Key Research Program of Frontier Sciences of CAS, the Fundamental Research Funds for the Central Universities.
（edited by YE Zhenzhen, USTC news center）
On May 11, the Nature Publishing Group released Nature Publishing Index 2010 China, remarking “a dramatic rise in the quality of research being published by China”. University of Science and Technology of China is ranked 3rd of TOP 10 Institutions in Index 2010 China.
This article came from News Center of USTC.